The purpose of this study was to evaluate the color changes of feldspathic ceramics CEREC Blocs (Dentsply Sirona, Milford, DE, USA) when cemented with different luting agents, while varying the ceramic thickness. Seventy ceramic discs of feldspathic ceramic (A2 shade) were obtained with 0.5 and 0.8 mm thicknesses. Seventy composite discs (A3 shade) 1 mm in thickness were used as substrates. After being polished and conditioned, the ceramic and composite discs were cemented with different resin cements and a flowable composite: Variolink® Esthetic Light, Neutral and Warm (Ivoclar Vivadent, Schaan, Liechtenstein); RelyXTM Veneer B0.5, Translucent and A3 Opaque/yellow shades (3M Oral Care, St. Paul, MN, USA); G-aenial® Universal Flow A2 (GC Europe, Leuven, Belgium). Color difference (ΔE) was determined using a spectrophotometer. A two-way ANOVA and multiple comparisons were performed using the Bonferroni method with a 95% confidence interval. Variolink® Neutral showed the highest ΔE (15.12 ± 0.71) and RelyXTM Veneer A3 the lowest value (1.59 ± 0.33). There are no statistically significant differences between the two ceramic thicknesses for Variolink® Light (p = 0.230) and RelyXTM Veneer B0.5 (p = 0.318) cements. The feldspathic ceramic final color is influenced by the cement used and the ceramic thickness. The use of different cements in a thin ceramic has a clinically significant impact on the final esthetic result.
RESUMO
OBJECTIVE: The purpose of this study is to evaluate the color changes of lithium disilicate ceramics when cemented with different brands of cement by varying the thickness of the ceramic. MATERIALS AND METHODS: Forty ceramic discs, shade A2, were fabricated with 0.5 and 0.8 mm thickness. Forty composite resin discs, shade A3, were also produced. The ceramic samples were cemented to the composite resin discs, with two colors of resin cement, Neutral and Warm. A spectrophotometer evaluation was made. Translucency and color change analysis was performed by calculating the ΔE. A two-way analysis of variance test and multiple comparisons were performed using the Bonferroni method with a 95% confidence interval. RESULTS: There are statistically significant differences between the two ceramic thicknesses with different brands of cement (p < .001). In addition, using the translucency analysis it was found that there are statistically significant differences between the two ceramic thicknesses in both types of cement (p < .001). CONCLUSIONS: The use of different cementation materials on lithium disilicate ceramics appears to have little visible influence at the clinical level. Different ceramic thicknesses have a clinically visible influence on the final restoration color.